DEKA ER70S-6, 3Si1 wire is used for semi-automatic welding of carbon and low-alloy steels in shielding gases: 100% CO2, 80% Ar + 20% CO2. Micropolishing of the wire surface with a special chemical composition increases the conductivity of the wire, reduces the energy required for welding and improves the mechanical characteristics of welds. The absence of shedding of copper coating in the feed mechanisms, along with a low friction coefficient, reduces downtime of welding equipment related to periodic cleaning of guide channels/hoses and increases the lifetime of the tip.

Chemical composition, %:
C ≤0,10
Si 0,60 – 0,85
Mn 1,40 – 1,70
P ≤ 0,030
S ≤ 0,025
Ni ≤ 0,25
Cr ≤ 0,20

Benefits of usage:

• Absence of shedding that leads to clogging of the feeding mechanisms.
• There are no additional short circuits when working at high currents.
• Cheaper than copper-clad wire
• Welding torch consumables last longer
• Reduced harmful effects on the body due to the lack of coverage
• Can be used for almost any type of welding
• Has a wide temperature range of use.
• Large range of products.

Available diameters: 0.8 mm, 1.0 mm, 1.2 mm, 1.6 mm and intermediate diameters.

Made in St. Petersburg

DEKA ER70S-7, 4Si1 wire is used for semi-automatic welding of carbon and low-alloy steels in shielding gases: 100% CO2, 80% Ar + 20% CO2. Micropolishing of the wire surface with a special chemical composition increases the conductivity of the wire, reduces the energy required for welding and improves the mechanical characteristics of welds. The absence of shedding of copper coating in the feed mechanisms, along with a low friction coefficient, reduces downtime of welding equipment related to periodic cleaning of guide channels/hoses and increases the lifetime of the tip.

Chemical composition of ER70S-7, 4Si1, %:

C 0,05 – 0,11
Si 0,7 – 0,95
Mn 1,8 – 2,1
P ≤ 0,030
S ≤ 0,025
Ni ≤ 0,075
Cr ≤ 0,2

Benefits of usage:

• Absence of shedding that leads to clogging of the feeding mechanisms.
• There are no additional short circuits when working at high currents.
• Cheaper than copper-clad wire
• Welding torch consumables last longer
• Reduced harmful effects on the body due to the lack of coverage
• Can be used for almost any type of welding
• Has a wide temperature range of use.
• Large range of products.

Available diameters: 0.8 mm, 1.0 mm, 1.2 mm, 1.6 mm, 2.0 mm and intermediate diameters.

Made in St. Petersburg

Polished steel welding wire EM12K, S2 is made for gas shielded and submerged arc welding.
During the production of polished wire DEKA in the technological process, instead of the copper plating process, the process of micropolishing the surface of the wire with a special chemical composition is used. That increases the current conductivity of the wire, reduces the energy required for welding and improves the mechanical characteristics of welds. The absence of shedding of copper coating in the feed mechanisms, along with a low friction coefficient, reduces downtime of welding equipment related to periodic cleaning of guide channels/hoses and increases the lifetime of the tip. Polished welding wire DEKA is used:

• For bridge structures welding
• For pipelines welding
• For containers and boilers welding
• For structures made of steel profiles welding
• For housings, frames and pipes welding

Chemical composition of EM12K, S2, %:
C ≤0,10
Si ≤0,06
Mn 0,8 - 1,1
P ≤0,030
S ≤0,025
Ni ≤0,25
Cr ≤0,10
Mo ≤0,15

Advantages of using DEKA polished wire:

• Absence of shedding that leads to clogging of the feeding mechanisms.
• There are no additional short circuits when working at high currents.
• Can be used for almost any type of welding.
• Has a wide temperature range of use.

Available diameters: 2.0 mm, 3.0 mm, 4.0 mm, 5.0 mm and intermediate diameters.

Made in St. Petersburg

Polished steel welding wire S2Ni1Mo, EA2 is made for gas shielded and submerged arc welding.
During the production of polished wire DEKA in the technological process, instead of the copper plating process, the process of micropolishing the surface of the wire with a special chemical composition is used. That increases the current conductivity of the wire, reduces the energy required for welding and improves the mechanical characteristics of welds. The absence of shedding of copper coating in the feed mechanisms, along with a low friction coefficient, reduces downtime of welding equipment related to periodic cleaning of guide channels/hoses and increases the lifetime of the tip. Polished welding wire DEKA is used:

• For bridge structures welding
• For pipelines welding
• For containers and boilers welding
• For structures made of steel profiles welding
• For housings, frames and pipes welding

Chemical composition S2Ni1Mo, EA2, %:
C 0,07 - 0,12
Si 0,11 - 0,35
Mn 0,4 - 0,7
P ≤0,020
S ≤0,025
Ni 1,0 -1 1,5
Cr ≤0,20
Mo ≤0,4 - 0,55
Advantages of using DEKA polished wire:

• Absence of shedding that leads to clogging of the feeding mechanisms.
• There are no additional short circuits when working at high currents.
• Can be used for almost any type of welding.
• Has a wide temperature range of use.

Available diameters: 2.0 mm, 3.0 mm, 4.0 mm, 5.0 mm and intermediate diameters.

Made in St. Petersburg